Effect of Aceton-Formaldehyde Resin Addition on Bonding Strength of Urea-Formaldehyde Resin Adhesive

요소수지(尿素樹脂)의 접착력(接着力)에 미치는 아세톤수지(樹脂) 첨가(添加)의 영향(影響)

Thermoplastic aceton-formaldehyde resin adhesive was added as a modifier for urea-formaldehyde resin adhesive and its effects on plywood smear strength and wood failure were investigated. The results are summarized as follows: 1) The plywood shear strength and wood failure showed the highest values at $120^{\circ}C$ of hot plate temperature, but the values decreased according to the rise of addition ratio of aceton resin. 2) The variation of molar ratio of aceton resin had no effect on plywood shear strength and wood failure. 3) The plywood bonded by the addition of aceton resin showed lower values than those of urea resin bonding plywoods in shear strength and wood failure. Therefore, aceton resin was inadequate as a modifier of urea resin adhesive.

요소수지(尿素樹脂)의 변성제(變性劑)로서 열가망성(熱可望性)의 아세톤수지(樹脂)를 첨가(添加)하고 합판(合板)의 접착력(接着力) 및 목파율(木破率)에 미치는 영향(影響)을 조사(調査)하였다. 결론(結論)을 요약(要約)하면 다음과 같다. 1) 합판(合板)의 접착력(接着力)과 목파율(木破率)은 열판온도(熱板溫度) $120^{\circ}C$에서 제조한 것이 가장 좋은 값을 보였으나 아세톤수지(樹脂)의 혼합비율(混合比率)이 증가(增加)함에 따라서 그 값은 점차 감소(減少)되었다. 2) 아세톤수지(樹脂)의 몰비율(比率)은 합판(合板)의 접착력(接着力) 및 목파율(木破率)에 영향(影響)을 미치지 않았다. 3) 아세톤수지(樹脂)를 혼용(混用)한 합판(合板)은 요소수지(尿素樹脂)만으로 접착(接着)된 합판(合板)의 접착력(接着力) 및 목파율(木破率)을 능가하지 못했다. 따라서 아세톤수지(樹脂)는 요소수지(尿素樹脂)의 변성제(變性劑)는 부적당(不適當)하였다.