The change of the hardness and yield strength in the nickel electrodeposits depending upon the electrolysis condition

전해조건에 따른 니켈전착층의 경도와 항복 강도의 변화

The change of the hardness and yield strength depending upon the electrolysis conditions was investigated for Watts and bright nickel electrodeposits. The hardness of Watts nickel electrodeposits decreased with increasing current density in the range of 1-15A/Am2, while it increased with increasing bath temperature. The hardness of bright nickel deposits increased noticebly in comparison with that of Watts nickel electro-deposits. The hardness and the yield strength of the bright nickel electrodeposits increased considerably with decreasing current density and the highest value was obtained at the lowest current density (1A/dm2), while they decreased noticebly at the bath temperature of 80$^{\circ}C$ in comparison with that of 40-60$^{\circ}C$. The change of the hardness and the yield strength of bright nickel electrodeposits depending upon the electrolysis conditions could be mainly attributed to the variation of organic additives codeposited in the electrodeposits. The recrystallizatioin temperature(50% softening temperature) of the Wattss and the bright nickel electro-deposits was 520-280$^{\circ}C$ and 350-410$^{\circ}C$ respectively and then the recystallization temperature of bright nickel deposits was lower than that of the Watts nickel electrodeposits.