CaO MgO.$2SiO_2-Al_2O_3$ 계의 고용체 생성에 관한 연구

A Study on the Forming of Solid Solution in CaO.MgO.$2SiO_2-Al_2O_3$ System

  • 안영필 (한양대학교 무기재료공학과) ;
  • 김복희 (한양대학교 무기재료공학과)
  • 발행 : 1983.01.01

초록

This experiment was studied in the system of (1-x) CaO MgO $2SiO-Al_2O_3$ to investigate forming of solid solution. The technique empolyed was the well known water-quenching method. Differential thermal analysis of the each glass water quenched indicated that under 30 mole% $Al_2O_3$ was lowered with increasing of the amount of $Al_2O_3$ It was supposed by X-ray diffraction patterns of each specimen sintered at various temperature that only solid solution was formed under the 30mole % $Al_2O_3$ compositions solid solution and anorthite were formed at the 20mole% $Al_2O_3$ composition anorthite solid solution and spinel$(MgAl_2O_4)$ were formed over the 40mole% $Al_2O_3$ compositions. The maximum density and thermal expanison coefficient was 2.89g/cm 7.74x106./C$^{\circ}$ respectively in the composi-tion of 10 mole% $Al_2O_3$ . All the specimens showed linear thermal expansion behavior. Microhardness was as high as 850kg/nm2 in the composition of 5, 10, 20 mole % $Al_2O_3$ and dielectric constant was 7.3-6.9.

키워드

참고문헌

  1. U. S. patent 2920971 Method of making ceramics and product thereof S. D. Stookey
  2. Inorg. Mater. v.3 no.11 Anorthite-wall-astonite system glass crystallization in the presence of chromic oxide N. A. Tropov;G. V. Tigonen
  3. J. Cam. Ceram. Soc. v.45 The fabrication of glass-ceramics materials based on blast furnace slag-A Review J. A. Topping
  4. Ceram. Bulletin v.51 no.6 Glass ceramics from the system CaO-Al₂O₃-SiO₂ J. A. Topping
  5. Glass Technol v.14 no.5 The effect of fabrication variables on the properties of cordierite based glass-ceramics. Part 1. the effect of variations in heat treatment R. C. de Vekey;A.J. Majumdar
  6. Glass Technol v.15 no.3 The effect of fabrication variables on the properties of cordierite based glass-ceramics. Part 2. The effect of composition R. C. de Vekey;A.J. Majumdar
  7. J. Am. Ceram. Soc. v.39 no.11 The binary system anorthite-akermanite E. C. de Wys;W. R. Foster
  8. Am. J. Sci. v.274 Kinetics of crystal growth in the system CaMg₂$Si_6$O-CaAl₂Si$O_6$ R.J. Kirkpatrick
  9. J. Geo. Research v.18 no.32 Kinetics of crystal growth from silicate melts: Anorthite and Diopside R. J. Kirkpatric;G. R. Robinson;J. F. Hays
  10. J. of Metals, Transations Aime Optimum composition of blast furnace slag as deduced rom liquidus data for the quaternary system CaO-Mgo-Al₂O₃-SiO₂ E. F. Osborn;R. C. DeVries;K. H. Gee;H. M. Kraner
  11. Am. J. Sci. v.279 Activity-composition relationships in Ca(Mg,Fe) Si₂$O_6$-CaAl₂Si$O_6$ clinopyroxene solid solutions B. J. Wood
  12. Min. Mag. v.21 The system diopside-anorthite-akermanite E. C. de Wys;W. R. Foster
  13. 日本特許昭 46-20718 透煐石燒結體の製造法 野元堅一郞
  14. Ceram. Bulletin v.50 no.6 Anorthite ceramic dielectrics R. A. Gdula