Effect of the grain size of temperature dependence on the creep behavior of SUS 316

SUS 316 강의 온도의존성 결정입경이 크리이프 거동에 미치는 영향

Austenitic stainless steel has been investigated widely for creep strength of heat resistant material and effects of grain sizes due to various solution treatment time under constant temperature. It was studied that effects of grain sizes subject to solution treatment temperature 1100.deg. C, 1125.deg. C, 1175.deg. C, 1250.deg C, and 1300.deg. C respectively on the creep strength, fracture behaviour and fractography of SUS 316 stainless steel. The experimental results obtained were as follows. 1. The optimum grain size for the maximum creep strength did not vary with creep testing temperatures and stress levels. 2. Among various grain sizes due to different solution treatment temperature, the optimum grain size for the creep strength was found 0.044mm. Also the size showed the minimum initial strain regardless creep temperature. 3. Garofalo's equation of creep rupture life was applied well to SUS 316 stainless steel. 4. The fractography of optimum size was ductile intergranular fracture of dimple type and showed along with the increase of grain size intergranular fracture of w type.