A Comparative Study on the Effect of Fire Retardancy of the Plywood Treated by Ammonium Sulphate and Monoammonium Phosphate

황산암모늄과 제 1 암모늄처리(處理) 합판(合板)의 내화효과에 관(關)한 비교연구(比較硏究)

This experiment was carried out for diminishing the material loss and the damage of human life due to the fire disaster by treating plywood with fire retardant chemical solution. At this study, we observed and measured chemical retention, burning point, maximum flame length, flame exausted time, carbonized area, and weight loss of plywood treated by each solution of ammonium sulphate [$(NH_4)_2SO_4$] and monoammonium phosphate [$NH_4H_2PO_4$]. Obtained results at the study may be summarized as follows: 1. In case of monoammonium phosphate-treated plywood, every tested item of fire retardancy was shown more excellent at the 25% chemical concentration and shown also at 9 hours treatment except maximum flame length compared with ammonium sulphate-treated plywood. 2. However in case of ammonium sulphate-treated plywood, 6 hours treatment of fire retardancy was better than 9 hours treating time. 3. Monoammonium phosphate was generally better than ammonium sulphate in every tested item.

합판(合板)은 가연성(可燃性) 물질(物質)로서 건축물(建築物)의 내장(內裝)에 많이 사용(使用)되므로 각종(各種) 대형화재(大型火災)를 유발(誘發)하여 많은 인명(人命)과 재산(財産)의 손실(損失)을 초래(招來)하는 경우(境遇)가 있다. 따라서 본(本) 연구(硏究)에서는 이로 인(因)한 피해(被害)를 최대한(最大限)으로 줄이기 위한 목적(目的)으로 합판(合板)에 내화처리(耐火處理)를 실시(實拖)하였다. 이 연구(硏究)에서는 제 1 인산암모늄과 황산암모늄 용액(溶液)으로 처리(處理)한 합판(合板)의 약액흡수성(藥液吸收量), 착화시간(着火時間), 최고염(最高炎)의 길이, 잔화시간(殘火時間), 이면탄화율(裏面炭火率) 및 중량감소(重量減少) 등은 측정조사(測定調査)하였으며 황산암모늄과 제 1 인산암모늄의 처리효과(處理效果)를 비교(比較)하여 보았다. 그 결과(結果)를 요약(要約)하연 다음과 같다. (1) 제 1 인산암모늄 처리합판(處理合板)의 경우(境遇)에 있어서 25% 농도(農度)에서 내화성(耐火性)이 가장 우수(優秀)하였고 최고염(最高炎)의 길이를 제외(除外)한 모든 처리효과면(處理效果面)에서 처리시간(處理時間) 9시간(時間)에서 내화성(耐火性)이 가장 우수(優秀)하였다. (2) 황산암모늄 처리합판(處理合板)의 경우에 있어서는 6시간(時間) 처리(處理)가 9시간(時間)의 처리(處理)보다 내화성(耐火性)이 더욱 우수(優秀)하게 나타났다. (3) 제 1 안산암모늄과 황산암모늄의 처리효과(處理效果)를 비교(比較)하면 대체로 모든 처리효과(處理效果)에서 제 1 인산암모늄이 황산 암모늄보다 우수(優秀)한 것으로 나타났다.