A Study on the Taro Extension of UF and PF Resin Bonding Plywoods

요소(尿素) 및 석탄산수지(石炭酸樹脂) 합판(合板)의 토란증량(土卵增量)에 관(關)한 연구(硏究)

This study was carried out to examine the possibility to replace imported wheat flour with taro. Taro and wheat flour were used for the extenders after oven drying($100{\pm}3^{\circ}C$)and pulverized into 80-100mesh minute powder by laboratory willey mill. Urea- and phenol-formaldehyde resin adhesives were used for plywood manufacture, and the extending materials mixed with the extension at the ratio of 10, 20, 30, and 50% to each resin solution. The results obtained at this study were summarized as follows; 1) In dry and wet shear strength of urea-formaldehyde resin adhesive, taro showed very excellent bonding strength compared with wheat flour in all extending ratio. Therefore taro showed the possibility that be usable to taro in place of wheat flour. 2) In dry and wet shear strength of phenol-formaldehyde resin adhesive, in general, wheat flour showed higher bonding strength than taro. But in dry shear strength, taro showed higher shear strength than wheat flour in 30 and 50% extension.

본연구(本硏究)는 합판제조시(合板製造時) 증량제(增量劑)로 이용(利用)되고 있는 소맥분(小麥粉)을 토란(土卵)으로 대체(代替)하기 위한 가능성(可能性)을 규명(糾明)하기 위해 실시(實施)되었다. 토란(土卵)과 소맥분(小麥粉)은 건조기내(乾燥器內)에서 전건상태(全乾狀態)로 건조(乾燥)시킨 후(後) 실험용(實驗用) 분쇄기(粉碎機)로 80~100 mesh로 분말화(粉末化)하여 증량제(增量劑)로 사용(使用)하였다. 합판제조(合板製造)에는 요소(尿素) 및 석탄산수지(石炭酸樹脂)를 사용(使用)하였으며 각수지(各樹脂)에 증량재료(增量材料)를 10, 20, 30, 50%의 비율(比率)로 혼합(混合)하여 시험(試驗)을 실시(實施)하였다. 본연구(本硏究)에서 얻어진 결론(結論)은 다음과 같이 요약(要約)할 수 있다. 1) 요소수지(尿素樹脂)의 상태(常態) 및 내수접착력(耐水接着力)은 모든 증량비율(增量比率)에서 토란(土卵)이 소맥분(小麥粉)을 훨씬 능가(能加)하고 있었다. 따라서 토란(土卵)은 소맥분(小麥粉)을 대체(代替)할 수 있는 가능성(可能性)을 보였다. 2) 석탄산수지(石炭酸樹脂)의 상태(常態) 및 내수접착력(耐水接着力)은 일반적(一般的)으로 소맥분(小麥粉)이 토란(土卵)보다 높은 접착력(接着力)을 나타내었다. 그러나 상태접착력(常態接着力)의 경우 30%와 50%의 증량(增量)에서는 토란(土卵)이 소맥분(小麥粉)보다 좋은 접착력(接着力)을 보였다.