Effects of the Water Reducing Agent on the Concrete

減水劑가 콘크리트에 미치는 影響

A study on the effect of water reducing agent on the various characteristics of concrete has been conducted. The experimental results of the study are summarized as follows. 1. Slump test for the concrete added water reducing setretarding agent in proper quantity have been conducted. According to the test results, the decreasing rate of slump value become bigger than plain concrete with increase of the unit weight of cement and elapse of time 2. In case the proper quantity content of maximum compressive strength in Fig. 5 of water reducing set retarding agent is added, unit weight of water is decreased about 15% or so as compared with plain concrete. with the increase of water reducing set accelerating agent content unit weight of water is decreased much more, And other hand, amount of air entraining shows the increasing tendency with the increase of water reducing agent content. 3. The adding rate of water reducing agent which produce maximum strength shows that WR-CH and WR-SA which is water reducing set-starding agent is 0.2% and WR-CO is 0.5% and that WS-PO which is water reducing set accelerating agent is 0.5 4. compressive strength jof the concrete made of sulfate resistant cement shows less than the strength of normal portland cement at initial strength but the strength of both cement shows almost same at curing age of 28 days. 5. when proper quantity of water reducing set retarding agent is used, boned strength is increased about 15% at curing age of 28days. 6. According to the result of durability test, dynamic young's mudulus of elasticity at plain concrete is decreased about 50% as compared with initial step at 300 cycle of freezing and thawing after curing age of days. on the contarary the concrete used water reducing agent is decreased less than 7%.