Abstract
The copolymerization of N-acryloylpyrrolidone and acrylonitrile was performed in N,N'-dimethylformamide at 50$^{\circ}$C and monomer reactivity ratio was obtained by using IR working curve and Fineman and Ross equation. ($r_1$ = 0.43, $r_2$ = 1.56) It is found that resulting copolymer is good polymeric initiator for anionic graft copolymerization of 2-pyrrolidone. Graft copolymers with polybutylamide (nylon-4) grafts onto poly(NAP-Co-AN) backbone were synthesized and the various effects on the graft copolymerization of 2-pyrrolidone were examined. The rate constants ($K_p$) of graft anionic polymerization at 40 and 50$^{\circ}$C were 2.82${\times}$10 and 2.93${\times}$10(l/mole, min), respectively.
N-acryloylpyrrolidone과 acrylonitrile을 혼성중합시켜 각 단위체의 반응성비를 구한 결과 생성되는 혼성중합체는 pyrrolidone이 음이온 중합에 매우 좋은 개시제임을 알 수 가 있었다. ($r_1$ = 0.43과 $r_2$ = 1.56) 그리고 그 혼성중합체를 개시제로 하여 그라프트된 nylon-4를 합성하여 중합속도 상수를 구했으며, 그에 따르는 여러 인자들의 효과를 관찰하였다. 그 결과 중합속도 상수로 40$^{\circ}$C에서 2.82${\times}10^3$(l/mole, min)와 50$^{\circ}$C에서 2.93${\times}10^3$(l/mole, min)을 얻었다.