Abstract
The effects of$ Fe_2O_3$ aggregation on the sintering of Ba-ferrite (BaFe$_{12}O_{19}$) were studied. $BaCO_3-Fe_2O_3$ mixtures were prepared by partial precipitation mixing and ball-mill mixing method using two different $Fe_2O_3 $powders. Techniques employed were TG, XRD and SEM. X-ray diffraction analysis showed that the over all reaction basically consists of the two consecutive reaction; $BaCO_3 + 6Fe_2O_3\;{\longrightarrow}\;BaFe_2O_3 + 5Fe_2O_3 + CO_2{\uparrow}\;BaFe_2O_4 + 5Fe_2O_3 \;{\longrightarrow}\;BaFe_{12}O_{19}$ It is also shown that the aggregation state of $Fe_2O_3$ raw materials, as well as the mixing method, has a remarkable effect on solid state reaction between $BaCO_3\;and\;Fe_2O_3$.
일차입자의 크기와 응집상태가 다른 두 종류의 $Fe_2O_3$를 부분침전법과 ball-mill 혼합법으로 BaCO$_3$와 혼합한 $BaCO_3-Fe_2O_3$계의 고체반응에 있어 $Fe_2O_3$분체의 영향을 조사하였다. TG, XRD, SEM 등을 측정에 사용하였으며, X-선 회절분석결과 Ba-ferrite의 생성과정은 다음과 같은 연속적인 2단계로 이루어진다는 것을 알았다. $BaCO_3 + 6Fe_2O_3\;{\longrightarrow}\;BaFe_2O_3 + 5Fe_2O_3 + CO_2{\uparrow}\;BaFe_2O_4 + 5Fe_2O_3 \;{\longrightarrow}\;BaFe_{12}O_{19}$ 또 $Fe_2O_3$원료분체의 응집상태와 혼합방법은 고체반응에 현저한 영향을 미친다는 것을 확인했다.