Abstract
Kinetic studies were carried out on urethane polymerization reaction of hydroxyl-terminated polybutadiene with isophorone diisocyanate under presence of Hexogen as solid additive. The rate was found to increase with the amount of Hexogen added. However the rate acceleration was not a catalytic effect but solely due to an increase of activation entropy. The reaction was a good 2nd order process with nearly constant activation energy of 8.4 kcal/mole.
Solid인 Hexogen 존재하에서 hydroxyl-terminated polybutadiene과 isophorone diisocyanate의 혼성중합반응속도에 관하여 연구하였다. 중합반응속도는 Hexogen의 첨가량이 증가할 수록 빠르게 나타났지만, Hexogen의 촉매적 역할은 없었으며, 오직 entropy control에 의한 반응임을 밝혔다. 이 반응은 2차 반응속도법칙에 잘 일치하며, activation energy는 8.4 Kcal/mole로 거의 일정하다.