Redrying Fire - Retardant - Treated Structural Plywood

구조용(構造用) 내화처리(耐火處理) 합판(合板)의 재건조(再乾燥)에 관(關)한 연구(硏究)

Exterior grades of Douglas-fir and aspen plywood were impregnated with interior fire-retardant chemicals and redried under low-, intermediate-, and high-temperature drying conditions. Fire-retardant treatments included borax-boric acid, chromated zinc chloride, minalith, pyresote, and a commercial formulation. Drying processes included kiln and press-drying. Evaluated were drying rates and defects generated. The borax-boric acid and the commercial treatments redried at rates similar to water-treated controls. Other salt treatments were significantly slower drying and more defect prone. Chromated zinc chloride treatment was consistently the slowest drying and most defect prone. Press drying was three times faster at an equivalent temperature level. However, thickness shrinkage doubled because of 50 1b/in. platen pressure.

미송(美松) 및 포푸라 내수합판(耐水合板)을 내장용내화제(內裝用耐火劑)로 가압처리한 다음 저온(低溫), 중온(中溫) 및 고온건조상태(高溫乾燥狀態)에서 재건조(再乾燥)를 실시(實施)하였다. 붕사(硼砂)-붕산(硼酸), 크롬화(化) 염화아연, 미나리스, 파이레소오트 및 일종(一種)의 상업용(商業用) 내화제(耐火劑)로 내화처리(耐火處理)를 실시(實施)하였다. 건조방법(乾燥方法)은 키른건조(乾燥)와 열판건조(熱板乾燥)를 적용(適用)하였으며 건조속도(乾燥速度)와 건조결함(乾燥缺陷)에 관하여 검토(檢討)하였다. 붕사(硼砂)-붕산(硼酸)은 수분처리합판(水分處理合板)과 유사(類似)한 건조속도(乾燥速度)를 나타내었으나 기타(其他)의 내화제(耐火劑)는 일층(一層) 늦은 건조속도(乾燥速度)를 나타내었고 더 많은 건조결함(乾燥缺陷)을 일으키는 경향(傾向)이 있었다. 특(特)히 크롬화(化) 염화아연은 가장 건조속도(乾燥速度)가 느렸으며 가장 많은 건조결함(乾燥缺陷)을 일으키는 경향(傾向)이 있었다. 열판건조(熱板乾燥)는 키른 건조(乾燥)와 비교(比較)하여 같은 온도수준(溫度水準)에서 삼배(三倍)나 더 빨리 건조(乾燥)하였으나 열판압력을 50 $1b/in^2$(3.52$kg/cm^2$)를 적용(適用)하였기 때문에 두께 수축율(收縮率)은 이배(二倍)를 나타내었다.