Studies on the Asplund Pulping of Wood for Paper Pulp(II) -Effect of some cellulose stabilizers added to the alkaline chip-treatment and the peroxide bleaching on the quality of larchwood asplund pulps-

제지용(製紙用) 아스플룬드펄프 제조(製造)에 관한 연구(II) -일본 잎갈나무��의 알카리 전처리(前處理)와 아스플룬드 펄프의 과산화물(過酸化物) 표백(漂白)에서 셀룰로오스 안정제(安定劑)의 영향(影響)에 관하여-

  • Published : 1981.09.30

Abstract

A Japanese larch has been reforested very much in Korea, but it is not used as a wood resources for paper pulp by now. So this study is carried out to utilize the larchwood for paper pulp manufacture through the Asplund pulping process. The experiment on increasing in the brightness of the pulp is made through the addition of $MgSO_4$, $ZnSO_4$, $Al_2(SO_4)_3$, and KI as a cellulose stabilizer in chip treatment with caustic soda which is followed by high-temperature defibration and conventional peroxide bleaching (5% NaOH plus 2% additive salt per wood in cold pretreatment), or in high-consistency (30%) pulp bleaching of hydrogen peroxide and peracetic acid (100% acitve oxygen per lignin) for conventional one. The results obtained are as follows: 1. The solution of 0.5% additive salts had different pH by the sort of bases that was pH 5.7 in $MgSO_4$, liquor, pH 4.9 for $ZnSO_4$, and pH 2.9 for $Al_2(SO_4)_3$, and in the precepitation of bases which ranged to pH 6-13 for $MgSO_4$, pH 5-12 for $ZnSO_4$, and pH 3-10 for $Al_2(SO_4)_3$. 2. The cellulose stabilizer affective in high-consistency peroxide bleaching was KI, $MgSO_4$, and $ZnSO_4$, but has made a little improvement in de lignification and brightness of pulp in comparison with no addition. 3. The higher alkalinity in the chip treatment has made the higher strength and brightness of larchwood Aspiund pulp instead of downing the pulp yield. And the effective compound for cellulose stabilizer in caustic soda pretreatment of chip was $ZnSO_4$, $Al_2(SO_4)_3$ and KI in order for the conventional peroxide bleaching after Asplund pulping. 4. Therefore, the more effective additives for cellulose stabilization in high-temperature defibration of larchwood suppose to be $ZnSO_4$, $Al_2(SO_4)_3$, and KI, while KI and $MgSO_4$ for peroxide bleaching.

우리나라에 대량조림(大量造林)되어 있는 일본잎갈나무는 기계(機械)펄프의 수율(收率)과 백색도(白色度)가 낮아 펄프재(材)로 이용(利用)되지 못하고 있다. 일본잎갈나무의 펄프재(材) 자원화(資源化)와 해예동력(解穢動力) 절약(節約)을 위하여 제지용 Asplund 펄프제조(製造)에서 셀롤로오스 안정제(安定劑)로서 $MgSO_4$, $ZnSO_4$, $Al_2(SO_4)_3$, KI을 택하고 고농도(高濃度) 과산화수소표백(過酸化水素漂白)과 과초산표백(過酢酸漂白)에서 그의 효과(效果)를 조사(調査)하고, ��의 알카리전처리(前處理)와 셀룰로오스안정제(安定劑)를 첨가(添加)한 알카리 전처리가 Asplund 펄프의 기존과산화수소표백(旣存過酸化水素漂白)에 미치는 영향(影響)을 조사(調査)한 결과(結果) 다음과 같이 요약(要約)된다. 1. 0.5%의 셀룰로오스안정제(安定劑)는 염기(塩基)의 종류(種類)에 따라 PH가 다르고($MgSO_4$=PH 5.72, $ZnSO_4$=PH 4.95, $Al_2(SO_4)_3$=pH 2.85), PH에 따라 침전 PH 범위($MgSO_4$=PH6~13, $ZnSO_4$=PH5~12, $Al_2(SO_4)_3$=PH3~10)와 최대(最大)침전 PH($MgSO_4$=PH9~10, $ZnSO_4$=PH6~7, $Al_2(SO_4)_3$=PH3~4)가 달랐다. 2. 일본잎갈나무 Asplund펄프의 고온고농도(高溫高濃度) 과산화수소(過酸化水素) 및 과초산표백(過酢酸漂白)에서 유효(有效)한 셀룰로오스안정제(安定劑)로는 KI, $MgSO_4$, $ZnSO_4$였으나 그의 효과(效果)는 미미하였다. 3. ��의 알카리전처리는 무처리보다 기존과산화수소표백(過酸化水素漂白)에 효과적(效果的)이었으며, 펄프의 강도(强度)와 백색도(白色度)를 향상(向上)시켰으나 수율(收率)은 저하(低下)시켰다. 그러나 셀룰로오스안정제(安定劑) 첨가(添加)는 황산염(黃酸塩)으로 인한 PH저하(低下)를 초래하여 탄산(炭酸)소다 전처리수준(水準)이었으며 ��의 알카리전처리에 첨가(添加)한 셀룰로오스안정제중(安定劑中)에서 해섬후(解纖後)의 과산화수소표백(過酸化水素漂白)에 유효한(有效)한 ��은 $ZnSO_4$, $Al_2(SO_4)_3$와 KI였다. 4. 따라서 산화조건에 효과적(效果的)인 안정제(安定劑)는 KI, $MgSO_4$이나 환원조건에서는 착염(錯塩)인 Zn, Al 염(塩)과 KI가 효과적(效果的)인 것으로 생각된다.

Keywords