Fracture toughness of Low-carbon steel using J-intergral Principle

J-적분을 이용한 저탄소강의 파괴탄성치 결정

The fracture toughness of a hot rolled 100 mm thick SS41 steel plate was investigated for various crack ratios and thichnesses using the method of J-integral. The experiments were performed on an MTS machine and the crack initiation point was detected by using an electricl impedance method. The J-integral computed at the initiation point of the slow stable crack growth was almost constant within the range of crack ratios tested. The fracture toughness thus obtained was $J_{1c}/=27.0kgf/mm$ for specimens having fracture plane parallel to the rolling direction and 35.5kgf/mm for those perpendicular to the rolling direction. The J- integral computed at maximum load point was found to be unsuitable for fracture toughness determination, becaese of large variation depending on the crack ratio and thickness. It was also found that the slow stable crack growth increases as the thickness and/or crack ration of the specimen decrease.