Since the organophilic bentonite disperses well in polymer matrix, a composite material of polymer and bentonite was studied for its mechanical properties. To increase the degree of dispersion and the bond in forces to the polymer matrix, bentonite, encapsulated by imidazoline, was used as a filler. Polyethylene powder of particle size of 100 mesh was used, and organophilic bentonite, so-called bentone, whose particle size was 250 mesh was also used in this experiment. V-type mixer was used for mixing and Banbury mixer was used for melt-blending. The sample specimen were made by heating the mixture in the plate press, and the specimen were formed as a sheet, exactly the same as the mold on the plate. Tensile strength, bending strength and compressive strength were studied specially. Tensile strength, elongation rate, bending strength and bending rate at constant pressure were decreased as the filler content increased. Compressive strength was increased as the filler content increased.
친유기성 bentonite가 고분자 물질중에서 잘 분산된다는 성질을 이용하여 고분자 물질과 bentonite의 복합재를 제조하고 그 기계적 성질에 관해서 연구하였다. Bentonite는 고분자 물질내에서 분산과 결합이 좋아지도록 imidazoline으로 처리한 후 충진제를 사용하였다. 고분자 물질인 polyethylene은 입도가 100mesh인 것을 사용하였고 친유기성 bentonite 즉 bentone은 입도가 250mesh인 것을 실험에 사용하였다. 분말의 혼합에는 V형 혼합기를 사용하였으며 Banbury mixer로 용융 혼합 시켰다. 시편의 모양은 plate press에 시료를 놓고 열을 가하여 판상으로 제작하였다. 물성을 조사하기 위하여 인장 강도, 곡 강도, 그리고 압축 강도 시험을 하였다. 인장 강도, 연신율, 곡 강도, 그리고 일정한 하중에 대한 굴곡율은 충진제 증가에 따라 감소되었다. 또한 압축 강도는 충진제 증가에 따라 크게 증가 하였다.