Abstract
The strain ageing behaviour of Zircaloy-4 has been studied in the temperature range 175$^{\circ}C$ to 575$^{\circ}C$ for both quenched and annealed specimens. The strain ageing in quenched Zircaloy-4 was found in the temperature range 175$^{\circ}C$ to 50$0^{\circ}C$ and its Peak occured at 3$25^{\circ}C$ while the strain ageing in annealed specimens occured in the temperature range 175-575$^{\circ}C$, showing two peaks, one at 323$^{\circ}C$ and a higher one at 45$0^{\circ}C$. The peak at 3$25^{\circ}C$ in both quenched and annealed specimens is considered to be due to the segregation of interstitial oxygen atoms to cell walls during ageing. The peak at 45$0^{\circ}C$ in annealed specimens is considered to he due to the interaction of dislocations with Fe atoms. It has been found that strain ageing stress at ~30$0^{\circ}C$ in zirconium alloys is proportional to the square root of oxygen content.
질칼로이-4의 가공시효(strain ageing) 현상을 173-575$^{\circ}C$의 온도구간에서 소입된 시편과 소둔된 시편에 대해 각각 조사하였다. 소입된 질칼로이-4의 가공시효가 175-50$0^{\circ}C$구간체서 난타났으며, 3$25^{\circ}C$에서 극대값의 가공시효가 조사였었다. 반면 소둔된 시편의 경우엔 175-575$^{\circ}C$ 구간에 걸쳐 가공시효가 나타났으며, 이 온도구간 사이에 3$25^{\circ}C$ 및 45$0^{\circ}C$의 두 지점에서 극대값이 나타나는 것을 확인했다. 소입된 경우와 소둔된 경우에 모두 3$25^{\circ}C$에서 보인 가공시효의 극대값은 시효동안에 전위조직 속으로 침입형 산소원자들의 응집에 의한 결과로 고려되며 45$0^{\circ}C$에서 보이는 극대값은 철원자와 전위간의 작용에 기인된 것으로 해석된다. 질코늄 합금의 30$0^{\circ}C$ 근처에서 보이는 가공시효값은 첨가된 산소량의 평방근에 비례한다는 것이 확인됐다.