Abstract
The elution behaviour of molybdate and tungstate through anion exchange column has been studied at the various pH. A discussion is made to evaluate the equilibrium constants of the polymerization of these acids comparing with the behaviour of chromate ion and dichromate ion. The eqailibrium constants found at $20^{\circ}$ are $K = 4{\times}10^{53} for 7MoO_4^{2-} + 8H^+ {\longleftrightarrow} Mo7O_{24}^{6- }+ 4H_2O$$ K = 3{\times}10^{54} for 6WO_4^{2-} + 7H^+ {\longleftrightarrow} HW6O_{21}^{5-} + 7H_2O$ referring to this results the conditions of separation of tungstate and molybdate are obtained. iThe quantitative separations of carbonate, molybdate and tungstate from the pregnant solution have been established by anion exchange chromatography, using the $22 cm{\times}44.27 cm^2$ column of Rexyn 201. The optimum eluents for the quantitative separation of those ions are as follows; 0.2M solution of sodium chloride at pH 8 for carbonate, the mixture of 0.5 M ammonium chloride and 0.05 M sodium sulfate at pH 5 for molybdate and 0.5 M solution of ammonium chloride at pH 10 for tungstate. Tungstate is directly recovered from the pregnant solution as a form of ammonium paratungstate, by eluting with ammonium chloride solution.
용리액의 pH변화에 따른 몰리브덴산과 텅스텐산의 용리곡선과 이들 산의 분리조건을 얻었다. 이 용리곡선으로부터 이들 산의 중합반응의 평형상수를 크롬산과 중크롬산의 중합반응의 결과와 비교하여 계산했고 분리조건을 pregnant 용액 분리에 적용했다. 이때 얻은 이들산의 중합평형상수 값은 다음과 같다. $7MoO_4^{2-}+8H^+{\longleftrightarrow}Mo7O_{24}^{6-}+4H_2O K=4{\times}10^{53},$$6WO_4^{2-}+7H^+{\longleftrightarrow}HW_6O_{21}^{5-}+3H_2O K=3{\times}10^{54}.$ 이온 교환크로마토그라피를 이용하여 프레그난트용액중의 탄산염을 분리하는 데는 pH8의 0.2M 염화나트륨 용액을 사용했고 몰리브덴을 분리하는데는 pH5의 0.05M $Na_2SO_4+0.5M NH_4Cl$ 혼합용액을, 텅스텐을 분리하는데는 pH 10의 0.5M 염화암모늄 용액을 단계적으로 사용하여 정량적으로 분리했다. 이때 텅스텐은 염화암모늄 용액을 용리액으로 사용했기 때문에 직접 APT(Ammonium para-tungstate)형태로 얻어졌다.