Abstract
When mixture of p-phenylenediamine (PPD) and m-aminophenol (MAP) were reacted with formaldehyde (F) varying their amounts under $N_2$ stream at the temperature of -5∼0$^{\circ}$, addition condensation reaction occurred and brown colored resins(in some cases orange colored) were formed immediately. All resins thus formed were insoluble in most ordinary organic solvents and did not melt up to 300$^{\circ}$. When the resins were treated with dilute(7 %) aqueous sodium hydroxide solution, the adsorptivity of methylene blue on them showed marked improvement reaching as much as 80 mg of methylene blue on 1 g of the resin. On the other hand, in the case of bromophenol blue, its amount of adsorption appeared 250 mg per 1 g of the resin. The TGA under $N_2$ atmosphere indicated that the resin formed in molar ratio of 1 : 3 : 8 (PPD : MAP : F) showed the best heat-resistant property among others. About 40 % weight loss was observed for this resin at 900$^{\circ}$ with heating rate of 2$^{\circ}$ per minute.
p-Phenylenediamine(PPD) 및 m-aminophenol(MAP)를 몰비를 달리하면서, -5∼0$^{\circ}$, $N_2$ 기류중에서 일정량의 포르말린(이때 포름알데히드의 량은 PPD와 MAP 전량에 대하여 2배몰에 해당하는 량으로 고정)과 반응시키면 약간의 발열과 함께 급격히 부가축합이 진행되어 난용성인 갈색 내지 등색의 중합체를 생성한다. PPD:MAP의 몰비가 1:3, 1:2, 1:1의 것들을 180∼220에서 몰비가 2:1, 3:1의 것들을 250∼270$^{\circ}$에서 각각 암색으로 색변화를 이르킬 따름이며, 이 중합체들은 모두 300$^{\circ}$까지 용융하지 않는다. 이들 중합체의 메틸렌블루에 대한 흡착력은 N2 기류중에서 중합시킨것을 묽은(7%) 수산화나트륨으로 처리하였을때 현저히 흡착력이 증가되어 PPD-MAP-F(F;포름알데히드)의 몰비가 1:3:8 일때 수지 1g당 80mg의 메틸렌블루를 흡착하며, 브롬페놀블루에대한 흡착력은 PPD-MAP-F의 몰비가 2:1:6일때가 최고이며, 수지 1g당 250mg의 브롬페놀블루를 흡착한다. TGA에 의한 내열성실험에서는 PPD-MAP-F의 몰비가 1:3:8인 경우 가장 좋은 결과를 나타냈으며, $N_2$ 기류중 매분 2$^{\circ}$로 가열하였을때 900$^{\circ}$에서 45%의 중량손실을 나타내었다.