On Crystallization of Korean Bentonite Treated with Aqueous Sodium Hyeroxide Solution

국산 Bentonite의 수산화나트륨 수용액 처리에 의한 결정의 변화

  • Myun Sup Kim (Department of Chemical Engineering, Hanyang University)
  • 김면섭 (한양대학교 공과대학 화학공학과)
  • Published : 1973.02.28

Abstract

Korean bentonite was treated with aqueous NaOH solution under the reaction conditions such as concentration of NaOH, 0.5-6N; ratio of $Na_{2}O$ to $SiO_2$, 1-4; reaction time, 2-30 days; reaction temperature, $70^{\circ}C-90^{\circ}C$. The products were examined by X-ray diffraction patterns. When it was treated with 2N NaOH at $70^{\circ}C$, zeolite species $P_1$ was formed with good yield. In higher concentration and at higher temperature than above, zeolite species $P_1$ was converted to hyeroxysodalite. Together with these crystals, some faujasite type zeolite, sodium A zeolite, mordenite type zeolite etc. was formed depending upon reaction conditions.

우리나라 영일산 Bentonite를 0.5-6 N NaOH로 $70-90^{\circ}C$에서 $Na_2:SiO_2$의 비율로 $1:1{\sim}4:1$로 2-30일의 범위에서 처리하여 그 겨정성의 변화를 X선회절법으로 조사하였다. 그 결과 2N NaOH로 $70^{\circ}C$에서 Zeolite Species가 좋은 수율로 생성되었다. 그러나 NaOH의 농도가 더 크고 온도가 더 높으면 이 Zeolite는 Hydrozysodalite로 변한다. 이 결정 외에도 처리조건에 따라서는 raujasite, sodium A zeolite, mordemite등의 결정도 소량 생겼다.

Keywords

References

  1. Ind. Eng. Chem. Prod. Res. Develop. v.10 G.R. Youngquist;J.L. Allen;E. Joseph
  2. J. Amer, Chem. Soc. v.93 C.Chao;J.H. Lunsford
  3. J. Amer. Chem. Soc. v.65 R.G. Russell;D.W. Pearce
  4. Ind. Eng. Chem. Prod. Res. Develop. v.10 T. Imai;R.B. Anderson
  5. 日本工業化學雜誌 v.73 宮田康夫
  6. J. Amer. Chem. Soc. v.80 D.N.Stamires;J.Turkevich
  7. 본지 v.16 권이열;김면섭
  8. 日本工業化學雜誌 v.74 鈴木秀行;岩井考俊;鈴木敏悅;香山勳
  9. Amer. Min. v.52 K. Harada;S. Iwamoto;K. Kihara
  10. J. Chem. Soc. (London) R.M.Barrer
  11. Amer. Min. v.39 T.W. Harris;G.W. Brindley
  12. Min. Mag. v.30 D.S. Coombs