Studies on Increase of Timber Strength with Electric Osmosis of Resin

수지(樹脂)의 전기삼투(電氣滲透)에 의(依)한 목재강도(木材强度) 증대(增大)에 관(關)한 연구(硏究)

In order to see a possible strengthening of much injection of synthetic resin into timber by way of electric osmosis, Authors examined the change of the bending strength of the sample timber piece after being injected. 1. Three kinds of sample tree species, Pinus rigida, Magnolia and Populus were used and the size of the sample timber pieces was $30mm{\times}30mm{\times}330mm$. 2. Each of the electric osmosis was made with 250V of D. C. voltage and $0.01A/cm^2$ of the current for 2 hours and the experimenter hardened the injected resin by putting the sample in an oven of $120^{\circ}{\pm}2^{\circ}C$ temperature for 24 hours. 3. The size of the test sample piece for bending strength measurement was $20mm{\times}20mm{\times}320mm$ and Amsler type universal timber test machine was used for the measurement. 4. The strength difference between treated and untreated samples was as follows. Pinus rigida high sig. Magnolia None Sig. Populus Sig.

목재(木材)에 합성수지(合成樹脂)를 주입(注入)시키는데 전기삼투법(電氣渗透法)을 적용(週用)하여 실지(實地)로 주입(注入) 가능(可能)한 가를 실험(實驗)하고 주입후(注入後) 공시재(供試材)의 휨강도(强度)의 변화(變化)를 고찰(考察)한 것이다. 1. 공시수종(供試樹種)은 리기다소나무, 일본목련, 이태리포푸라이다. 2. 공시편(供試片)의 크기는 $30mm{\times}30mm{\times}330mm$ 이다. 3. 직류전압(直流電壓) 250V, 사용전류(使用電流) $1cm^2$당(當) 0.01A로 2시간(時間) 처리(處理)한 후(後) $120^{\circ}{\pm}2^{\circ}C$의 Oven에 넣어 24시간(時間) 경화처리(硬化處理) 하였다. 4. 휨 강도(强度) 측정(測定)의 시편(試片)은 $20mm({\times}20mm{\times}320mm$로 하고, Amsler식(式) 목재만능시험기(木材萬能試驗機)를 사용(使用)하였다. 5. 처리재(處理材)와 비교재간(比較材間)의 강도(强度)의 유의차(有意差)는 다음과 같다. a. 리기다소나무에 있어서는 고도(高度)의 유의차(有意差)가 있었다. b. 일본목련에 있어서는 유의차(有意差)가 나타나지 않았다. c. 이태리포푸라에 있어서는 5%수준(水準)에서 유의차(有意差)가 있었다.