Abstract
The Capacity of wood to absorb water is very important as the basis data for wood industry, particularly in preservatives impregnation, manufacturing of improved wood, selection of packing boards, etc. In this study differences in Water absorbing Capacity of wood by structual section, water soaking time were investigated. (1) The species used in this investigation were Larix olgensis Henry Var. Koreana Nakai and Juglans mandshurica Max., and dimension of these testing wood block was $30{\times}30{\times}100cm$; and these were soaked in fresh water of $25{\pm}1^{\circ}C$ for 8.5day and 0.5 day, before measurement. (2) The result showed that the water absorption by cross sections was greater than by either radial or tangential section and there were no differences between radial and tangential section. (3) The water absorption of Juglans mandshurica Max. which has the relatively low specific gravity was greater than Larix olgensis Henry Var. Koreana Nakai which has generally high specific gravity. (4) The result showed an increase in the absorbed water with increase in the length of soaking time. However the water absorption rate during the early period of soaking was very high and thereafter the rate decreased with passage of time. More than a half of the total water absorption was achieved during the first 2 days approximately. (5) The relationships between the length of the soaking-time and water absorption were found to be as follows : Larix olgensis Henry Var. Koreana Nakai Cross section : $y=111.1{\times}^{0.6516}$ radial section : $y=32.2{\times}^{0.5146}$ tangential section : $y=36.5{\times}^{0.5112}$ Juglans mandshurica Max. Cross section : $y=216.1{\times}^{0.5914}$ radial section : $y=27.9{\times}^{0.5832}$ tangential section : $y=50.9{\times}^{0.4769}$ Where : y is amount of water absorption ($mg/cm^2$) x is water-soaking time (days).
본(本) 대학(大學) 연습림(演習林)에서 생육(生育)한 32년생(年生) 잎갈나무와 27년생(年生) 가래나무를 이용(利用)하여 시험(試驗)한 목재(木材)의 구조단면별(構造斷面別) 흡수성(吸收性) 및 수침시간(水浸時間)에 의(依)한 단면별(斷面別) 흡수성(吸收性)을 요약(要約)하면 다음과 같다. (1) 본시험(本試驗)에 사용(使用)한 시편(試片)($30{\times}30{\times}100cm$)을 각(各) 단면별(斷面別)로 흡수면(吸水面)만 남기고 paraffin과 vaseline과의 등량혼합물(等量混合物)로 방수(防水)하여 $25{\pm}1^{\circ}c$의 청수(淸水)에 8.5일간(日間) 침지(浸漬) 0.5일(일)(12시간)마다 중량(重量)을 측정(測定)하여 흡수성(吸水性) 조사(調査)하였다. (2) 목구면(木口面)에서의 흡수성(吸水性)은 구목면(柾目面)이나 구목면(柾目面)의 종단면(縱斷面)에서의 흡수성(吸水性)보다 대단(大端)히 크며 구목면(柾目面)과 판목면(板目面)에 있어서는 차이(差異)가 거의 없다. (3) 가래나무의 구목면(柾目面)을 제외(除外)하고는 비중(比重)이 비교적(比較的) 적은 가래나무가 비중(比重)이 보다 큰 잎갈나무보다 각(各) 단면(斷面)에서의 흡수성(吸水性)이 크다. (4) 침지시간(浸漬時間) 경과(經過)함에 따라 흡수성(吸水性)이 증가(增加)된다. 또한 침지초기(浸漬初期)에는 흡수성(吸水性)이 대단(大端)히 크나 시간(時間)이 경과(經過)함에 따라 그 정도(程度)는 점차(漸次) 감소(減少)된다. 흡수율(吸水率) 약(約) 반(半) 이상(以上)은 대게 침지(浸漬) 48시간(時間) 전후(前後)의 초기(初期)에 이루어진다. (5) 목구면(木口面)에서는 침지시간(浸漬時間)이 경과(經過)함에 따라 잎갈나무와 가래나무의 흡수성(吸水性) 점차(漸次) 큰 차이(差異)를 나타내며 구목면(柾目面)에서는 초기(初期)의 다소(多少)의 차이(差異)가 있으나 시간(時間)이 경과(經過)함에 따라 아주 일치(一致)한다. (6) 침지시간(浸漬時間)과 흡수량(吸水量)사이에는 다음과 같은 실험식(實驗式)이 성립(成立)한다.