Abstract
The time-lag-effect of alkali salts on the gelation of sodium alginate-$CaSO_4{\cdot}$1/2 $H_2O$ is compared with Miyake's data, and then the formation rate of the elastics measured by the continuous method (an improved Schwedoff's method) and the change of rigidity with metallic oxides are studied as follows: (1) The gelation processes of sodium alginate and $CaSO_4{\cdot}$1/2 $H_2O$-aqueous sol are studied by measuring, continuously the increases of tensions ofsamples. (2) The time-lag-effect of $Na_3PO_4$ on the formation rate of the elastic gel is larger than that of $Na_2CO_3$, but the difference between the effects of the two alkali salts on the rate is found not so greater than predicted in Miyake's data. (3) Any regularities of the effect on the rate by metallic oxides are not observed. The increasing effects of the rates of $SiO_2$ and MgO are relatively large, and that of ZnO is relatively small. However, $Al_2O_3$, $Sb_2O_3$ and $TiO_2$show some decreasing effects. As a result it is noted that the regularities do not depend on the effect of oxide species and their amounts. (4) It is not found proportionality between the rigidity and the gelation rate. However, the increasing effect of the rigidity with the addition of metallic oxides can be observed. The rigidity increasing rate of MgO is the largest of them.
Sodium alginate-$CaSO_4{\cdot}$1/2 $H_2O$의 gel에 미치는 alkali鹽의 遲延효果를 Miyake date와 比較하고, Schwedoff法을 改良한 連續的 測定方法을 써서, 金屬酸化物의 添加에 依한 彈性 gel의 生成速度 및 彈性의 變化를 硏究하였다. 즉 (1) sample의 張力變化를 連續的으로 測定하여, sodium alginate와 $CaSO_4{\cdot}$1/2 $H_2O$ aqueous sol의 gel化 過程을 觀察하였다. (2) 彈性 gel의 生成速度에 미치는 $Na_3PO_4$의 遲延효果는 $Na_2CO_3$보다 크다는 點에서는 Miyake 報告와 一致하였으나, Miyake date처럼 兩者間에 그리 큰 差가 없었다. (3) 金屬酸化物이 彈性 gel生成速度에 미치는 影響에 어떤 規則性은 없었지마는 $SiO_2$와 MgO는 比較的 큰 速度增大효果를 나타내고 ZnO는 比較的 적었다. 그러나 $Al_2O_3$, $Sb_2O_3$와 $TiO_2$는 速度低下효果를 나타냈다. 結果的으로 酸化物의 種類나 그 添加量에 따라 어떤 明確한 規則性을 觀察하지 못하였다. (4) 彈性率과 生成速度에 미치는 효果사이에 比例關係는 없없으나 金屬酸化物을 添加하면 一般的으로 彈性率이 增加하였다. 이들 酸化物 中에서 彈性率增大효果가 가장 큰 것은 MgO였다.