Repair method application for micro-cracks of less than 0.3 mm width in residential apartment buildings

공동주택에 발생되는 0.3mm미만 미세균열의 보수공법 적용을 위한 근거 마련 기초연구

Cracks are typical defects that occur in concrete structures. When cracks occur in the structure, durability reduction, concrete neutralization, and steel corrosion cause functional safety problems. In order to prevent such cracks, surface repair method is performed for cracks smaller than 0.3 mm and rechargeable method is performed for cracks larger than 0.3 mm. However, even if it is applied by the surface repair method at less than 0.3 mm, re-leakage cracks continue to occur. Recently, the Supreme Court ruled that the rechargeable method should be applied to cracks less than 0.3mm in order to reduce the occurrence of defects. However, it was considered that the repair fees were too high relative to the observed defect rate, resulting in a necessitation of modifying the existing construction analysis administration standards. This study analyzes the differences in the subjective views on the durability degradation with regards to surface repair methods in concrete structures.