Atomic Layer Deposition for Energy Devices and Environmental Catalysts

  • 발행 : 2013.08.21

초록

In this talk, I will briefly review recent results of my group related to application of atomic layer deposition (ALD) for fabricating environmental catalysts and organic solar cells. ALD was used for preparing thin films of TiO2 and NiO on mesporous silica with a mean pore size of 15 nm. Upon depositing TiO2 thin films of TiO2 using ALD, the mesoporous structure of the silica substrate was preserved to some extent. We show that efficiency for removing toluene by adsorption and catalytic oxidation is dependent of mean thickness of TiO2 deposited on silica, i.e., fine tuning of the thickness of thin film using ALD can be beneficial for preparing high-performing adsorbents and oxidation catalysts of volatile organic compound. NiO/silica system prepared by ALD was used for catalysts of chemical conversion of CO2. Here, NiO nanoparticles are well dispersed on silica and confiend in the pore, showing high catalytic activity and stability at 800oC for CO2 reforming of methane reaction. We also used ALD for surface modulation of buffer layers of organic solar cell. TiO2 and ZnO thin films were deposited on wet-chemically prepared ZnO ripple structures, and thin films with mean thickness of ~2 nm showed highest power conversion efficiency of organic solar cell. Moreover, performance of ALD-prepared organic solar cells were shown to be more stable than those without ALD. Thin films of oxides deposited on ZnO ripple buffer layer could heal defect sites of ZnO, which can act as recombination center of electrons and holes.

키워드