Test Method for Composites Material Properties under High Temperature(I)

복합재의 고온 특성 평가를 위한 시험 기법연구(I)

The effect of high-temperature on the flexural modulus of epoxy resin were evaluated using universal testing machine with 3-point bending and dynamic mechanical analyzer. Temperatures of $30^{\circ}C$, $100^{\circ}C$, and $140^{\circ}C$ were considered for flexural test. The specimens having aspect ratio of 16, 32, and 40 were used. The results of storage modulus from DMA were similar to those from flexural test along with given temperatures. It is found that the flexural modulus increased with increasing aspect ratio and the specimen having aspect ratio of above 32 would be suitable for the evaluation of composite material properties under high temperature condition.

본 연구에서는 3점 굽힘시험 및 DMA 시험을 통해 온도환경이 에폭시 수지의 굽힘탄성계수에 미치는 영향을 조사하였다. 굽힘 시험의 온도 조건은 $30^{\circ}C$, $100^{\circ}C$, $140^{\circ}C$의 세 가지 조건을 적용하였으며 시편은 종횡비 16, 32, 40배의 세 가지 종류가 고려되었다. 연구결과에 따르면 DMA를 통한 저장탄성계수와 굽힘시험을 통해 얻은 강성은 주어진 온도조건에서 서로 유사한 경향을 보였다. 또한 종횡비가 증가함에 따라 굽힘탄성계수도 증가 하였으며, 고온환경에서는 32배 이상의 종횡비가 적합하다고 판단된다.