Effect of Substrate Temperature on Polycrystalline Silicon Film Deposited on Al Layer

Al 박막을 이용한 다결정 Si 박막의 제조에서 기판온도 영향 연구

The surface morphology and structural properties of polycrystalline silicon (poly-Si) films made in-situ aluminum induced crystallization at various substrate temperature (300~600) was investigated. Silicon films were deposited by hot-wire chemical vapor deposition (HWCVD), as the catalytic or pyrolytic decomposition of precursor gases SiH4 occurs only on the surface of the heated wire. Aluminum films were deposited by DC magnetron sputtering at room temperature. continuous poly-Si films were achieved at low temperature. from cross-section TEM analyses, It was confirmed that poly-Si above $450^{\circ}C$ was successfully grown on and poly-Si films had (111) preferred orientation. As substrate temperature increases, Si(111)/Si(220) ratio was decreased. The electrical properties of poly-Si film were investigated by Hall effect measurement. Poly-Si film was p-type by Al and resistivity and hall effect mobility was affected by substrate temperature.