Characterization of $Cu_2ZnSnSe_4$ thin film produced by selenization of metallic precursor

금속 프리커서의 셀렌화에 의한 $Cu_2ZnSnSe_4$ 박막의 특성

  • Published : 2010.06.17

Abstract

$Cu_2ZnSnSe_4$ (CZTSe) is one of candidate to alternate $Cu(In,Ga)Se_2$ as solar absorber material for solar cell. The expensive elements of In and Ga are replaced by Zn and Sn, respectively to lower the material cost. In this study we fabricated CZTSe thin film by selenization of single precursor layer consisted metallic constituent. Precursor compositions ratio were selected to have Cu-poor and Zn-rich content and prepared by RF magnetron sputtering. Thermal processing was applied to introduce selenium into as-deposited films at temperatures ranging from 350 to 500 for time up to 120 minutes. Single precursor films showed amorphous structure and consist of individual elements of Cu, Zn, and Sn. It was confirmed by XRD analysis that synthesis of CZTSe compound is occurred from lower temperature process, although concurrently additional phases such as binary cooper selenides are also existed. The quality of CZTSe crystal was improved as temperature increased. We also investigated the optical and electrical properties of as-selenized CZTSe as well.

Keywords