초록
Recently, bulk hetero-junction cells have been extensively studied by many researchers. Most of these cells were fabricated by spin coater. However, the spin coating process is not favorable to the large-scaled industry because it is not compatible with roll-to-roll process. One of the alternative methods is Doctor blading. In this study, we fabricated large OPV cells having total area of $100cm^2$. The buffer layer was Poly-(3,4-ethylenedioxythiophene) : poly-(styrenesulfonate) aqueous dispersion (PEDOT:PSS) and the active material is poly (3-hexythiophene) (P3HT) and phenyl-C61-butyric acid methyl ester (PCBM) blend in the solvent of Chlorobenzene. All of the organic layers were coated by dragging the blade with a speed of 5~20 mm/s on the stage with a temperature of $50^{\circ}C$. As-bladed PEDOT:PSS layer was baked at $120^{\circ}C$ for 10 minutes to eliminate the water. The cell structure is patterned ITO substrate/PEDOT:PSS/P3HT:PCBM/LiF/Al. The topmost electrode, LiF/Al, was deposited by thermal evaporation. After depositing electrode, and the cell was annealed at $150^{\circ}C$ for 30 minutes. The measured ISC, VOC, fill factor, and PCE were 2.95 A, 5.86 V, 0.32, and 0.78%, respectively. PCE was quite low but the large active area could be obtained successfully.