Influence of subsequent-annealing on the oxide layer of AZ91 Mg alloy prepared by plasma electrolytic oxidation

PEO 코팅 처리된 AZ91 합금의 산화층에 미치는 후-열처리의 영향

The influence of the subsequent-annealing (SA) treatment on plasma electrolytic oxidation (PEO)-treated Mg-based alloy was investigated and the dependence of the dehydration reaction on the SA temperature was also studied. For this purpose, a series of the SA treatments were carried out on the coated samples at two different temperatures, i.e. 423 and 523 K for 10 h. In contrast to the sample without SA treatment, the sample annealed at 523 K exhibited a significant difference in term of surface morphology since the MgO content in the oxide layer increased with increasing SA temperature. With increasing SA temperature, the dehydration of $Mg(OH)_2$ led to the increase in the relative amount of the MgO, which was a hard phase. From the nano-indentation results, the applied loads of the samples were seen to increase as SA temperature increased. However, the corrosion resistance of the sample annealed at 423 K was higher than that of the samples annealed at 523 K.