Weld Quality of MCFC Separators With Large Active Area

MCFC용 대면적 분리판의 용접부 품질에 관한 고찰

Quality evaluation of laser welded MCFC separator panels with large active area was performed. Lap joint was applied to produce stable air-tight seam weld by employing Nd:YAG laser. Results showed that surface contamination played a key role to form weld defects at the joint interface. However, there was no evidence that weld width at the lap joint changed after the stack operation time of 2,890h. Test results also revealed that the reinforcement values which were measured on the weld line after long time operation, were stable.