A Study on Mechanical Properties of High Strength Concrete Performed by Full Scaled Mock-up Test

1:1 실부재 Mock-up Test를 통한 고강도 콘크리트의 역학적 특성에 관한 연구

The super tall building above 100 floors is required that each floor's height is more than 4 meters, and each core wall's thickness is more than 60cm. Therefore, for the successive accomplishment of super tall building, the full scale mock-up test was required. The test results are as follows; Real strength of core wall was satisfied with design strength at 28 days regardless of types of strength, and according to the consolidation effect, lower part's strength was a little higher than upper part's strength. Lateral force of HSC was evaluated with max. $4.5ton/m^2$, and hydration temperature of mock-up test was evaluated that maximun heat of central part revealed about $80^{\circ}C$ at 70MPa and $65^{\circ}C$ at 50MPa, and, the difference between inner and outter part revealed about $30^{\circ}C$ at 70MPa and $12^{\circ}C$ at 50MPa. Also, no crack by hydration temperature was not shown on the surface.

100층 이상 구조물은 1개층 높이가 최소 4m 이상이며, 코어월 벽체 두께가 60cm에서 최대 1.4m 정도 되는 매스콘크리트 구조물이다. 이러한 프로젝트를 성공적으로 수행하기 위하여 초고층 구조물 실제 부재를 감안하여 50MPa와 70MPa를 대상으로 각각 $4{\times}4{\times}0.6m$, $4{\times}4{\times}1.1m$ 의 실부재 사이즈의 Mock-up을 제작하여 각종 역학적 특성을 평가하였다. 평가결과는 다음과 같다. 코어강도의 경우 재령 28일에서 모두 설계기준강도를 만족하는 것으로 나타났으며, 압밀작용에 의해 코어 하부의 강도가 상대적으로 더 높게 나타났다. 콘크리트 측압은 최대 4.5Ton 정도로 나타났으며, 수화온도 측정결과의 경우 설계강도 70MPa는 최대온도 약 $80^{\circ}C$, 내외부 온도차 최대 $30^{\circ}C$ 정도 나타났고, 설계강도 50MPa의 경우는 최대온도 약 $65^{\circ}C$, 내외부 온도차 $12^{\circ}C$이내로 나타났다.