Effect of the Various Curing Temperatures on the Finishability of Concrete using Aluminum Form

알루미늄 거푸집을 이용한 콘크리트의 양생온도변화에 따른 표면마감성에 관한 연구

This study investigated the effect of the fundamental condition such as release agent, form conditions and types to the surface of concrete with aluminum form on the various temperatures. On the observation with the naked eyes, coated plywood and aluminum form without a scratch showed similar result, and the surface quality of the concrete with aluminum form was gradually decreased corresponding to the increase of the temperature.For the surface roughness, there is no remarkable tendency according to the temperature. However, the difference in accordance with release agent occurred.As void on the surface corresponding to the various temperature, the micro voids ranged $0.1{\sim}1mm$ were increased corresponding to the increasing temperature, so it was confirmed that the chemical reaction wae accelerated. And the voids of the other range also increased. the fundamental condition such as release agent, form conditions and types

본 연구는 온도변화에 따라 기초영향인자가 콘크리트와 알루미늄 거푸집간의 표면 마감성에 미치는 영향에 대하여 분석한 것으로 그 결과를 요약하면 다음과 같다. 육안관찰상 코팅합판과 무손상 알루미늄 거푸집의 경우 비슷한 결과를 나타냈으며, 온도변화에 따라서는 알루미늄 거푸집을 사용한 경우 온도가 높아질수록 표면품질이 약간씩 저하하는 것을 확인할 수 있었다. 표면조도의 경우 온도변화에 따른 차이는 거의 나타나지 않았으며, 박리제의 도포여부에 따른 차이가 발생하였다. 온도변화에 따른 표면공극분포는 온도가 증가할수록 $0.1{\sim}1mm$ 범위의 미세한 기포가 증가하여 화학반응이 촉진됨을 확인할 수 있었으며, 다른 범위의 공극도 증가하였다. 또한, 온도가 증가할수록 다른 인자들의 영향이 더욱 커지는 것을 확인할 수 있어 온도증가에 의해 알루미늄 거푸집을 이용하는 콘크리트의 표면품질이 저하함을 확인할 수 있었다.