Abstract
This study was achieved experiment to evaluate effect on fluidity and strength development ratio by slag replacement ratio to $40{\sim}100MPa$ HSC(High Strength Concrete) containing blast furnace slag(GGBS) and fly-ash(FA). Also it was suggested that most suitable replacement ratio of GGBS is effect by strength. The mix plan of concrete used in an experiment was used to the GGBS replacement ratio of 0, 12, 25% as the cement materials, and fly ash was used equally by replacement ratio 15%. According to test results, for use GGBS with fly ash as binder, slump of GGBS replacement ratio 25% is the most superior in 40MPa series, and appeared by thing which slump flow of GGBS 12% is the most superior in 60, 80MPa's series. The other side, was expressed that fluidity is excellent by FA replacement ratio 15% in 100MPa series. In the case of compressive strength 40MPa, it was exposed that the strength revelation is effect in until the GGBS principal parts ratio increases by replacement ratio 25%. Also, it was exposed that GGBS mixing ratio more than replacement ratio 25% is not since fitness in high strength concrete more than 100MPa.
본 논문에서는 압축강도가 $40{\sim}100MPa$인 3성분계 고강도콘크리트를 대상으로 혼화재의 대체율이 3성분계 고강도콘크리트의 유동성과 강도발현에 미치는 영향을 평가하기 위한 연구를 수행하고, 강도별 적정 혼화재 대체율을 제안하였다. 실험에 사용된 3성분계 고강도콘크리트의 배합 시 시멘트 대체재로써 고로슬래그가 0, 12, 25% 사용되었으며, 플라이 애시 대체율은 15%로 동일하게 계획하였다. 실험결과, 시멘트 대체재로써 고로슬래그를 플라이애시와 혼용하여 사용하는 경우 40MPa 시리즈에서 고로슬래그 대체율이 25%일때 슬럼프가 가장 우수하며, 압축강도 60, 80 MPa의 시리즈에서는 고로슬래그 대체율이 12%일때 슬럼프 플로우가 가장 우수한 것으로 나타났다. 반면 압축강도 100MPa의 경우 플라이 애시 15%만으로도 유동성이 가장 우수한 것으로 나타났다. 그리고 압축강도 40MPa의 경우 고로슬래그 대체율이 25%로 증가할 때까지 강도발현에 효과가 있는 것으로 나타났으며, 100MPa이상의 고강도콘크리트에서는 25% 이상의 고로슬래그 혼입률은 적합지 않은 것으로 나타났다.