The Properties of Compressive Strength of Non-standard Specimens Considered Strength Level

강도수준을 고려한 비표준형 공시체의 압축강도 특성

Recently as application of high-strength concrete on concrete structures has been on the rise, use of non-standard specimen is increasing. Therefore, this study investigated the effect of specimen's size effect, ratio of height/diameter and curing conditions on concrete compressive strength. Results of experiments showed that as size of specimen increased as much as 1 mm, standard design compressive strength of 24MPa fell as much as0.15MPa 40MPa fell as much as 0.1MPa 80MPa fell as much as 0.3MPa, and it indicates that as the level of strength is intensified, the decrement of compressive strength increases. As ratio of height/diameter increased as much as 1.0, compressive strength of 24MPa fell as much as 2.9MPa 40MPa fell as much as 3.7MPa 80MPa fell as much as 9.8MPa, and it means that as strength of concrete is higher, influence of ratio of height/diameter becomes bigger.

최근 고강도콘크리트의 현장적용이 증가하면서 현장 콘크리트의 품질확인을 위한 강도 측정시 고강도콘크리트 공시체와 안전진단시 채취되는 비표준형 공시체의 사용이 증가하고 있다. 이에 본 연구에서는 콘크리트의 가장 기본적인 재료특성인 압축강도 특성을 공시체에 대한 크기 효과와 강도수준을 고려하여 합리적인 관계식을 적립하고자 하였다. 실험결과, 공시체 크기 1mm 증가시마다 압축강도는 기준강도 24MPa에서 0.05MPa, 40MPa에서 0.1MPa, 80MPa에서 0.3MPa씩 감소시키는 것으로 나타나, 강도수준이 고강도화 될수록 압축강도 감소량은 증가하는 것으로 나타났다. 또한 공시체 높이/직경비가 1.0 증가시마다 압축강도는 24MPa에서 2.9MPa, 40MPa에서 3.7MPa, 80MPa에서 9.8MPa 감소되어 고강도콘크리트일수록 높이/직경비의 영향을 크게 받는 것으로 나타났다.