Effect of the Various Admixtures to Improvement of Concrete Using Over-added Blast Furnace Slag at Early Age

고로슬래그 미분말을 다량 사용한 콘크리트의 초기품질 향상에 미치는 각종 혼합재료의 영향

This study, with the purpose for early quality improvement of concrete which used large quantity of fly ash, changed various admixture material type and reviewed the basic characteristics. First off, the flow overall was highest when polycarb onic Acid high early strength AE water reducing agent was displaced, while air amount satisfied target level only in the case of plain, and setting time was shown best by getting 30 more minutes than plain and about 3 more hours than conventional when KOH is displaced. Compressive strength was shown best at age 1 day and 3 days when KOH was displaced, and at age 28 days when fine particle cement was displaced. By and large, this study concludes that concrete quality improvement admixture material that used large amount of fly ash showed worse effects than plain, therefore it is determined that there need be more study for development of concrete early quality improvement admixture material that used large amount of fly ash.

본 연구에서는 플라이애시를 다량 사용한 콘크리트의 초기 품질 향상을 목적으로 각종 혼합재료의 종류를 변화시켜 적정량을 혼입시킨 다음 그 기초적 특성을 검토하였는데, 그 결과를 요약하면 다음과 같다. 먼저, 유동성은 전반적으로 폴리칼본산계 조강형AE감수제를 치환한 경우 가장 크게 나타났고, 공기량에서는 Plain의 경우에만 목표 공기량을 만족하는 것으로 나타났으며, 응결시간은 KOH를 치환한 경우 Plain보다 30분, 기준배합보다 약 3시간 촉진되어 가장 양호한 효과를 발휘하는 것으로 나타났다. 압축강도는 혼합재료의 종류 변화에 따라서 재령 1일 및 3일에서는 KOH를 치환한 경우, 재령 28일에서는 미분시멘트를 치환한 경우 가장 양호하였다.