Properties of High Performance Concrete Corresponding to the Replacement Ratio of the Blast Furnace Slag

고로슬래그 미분말의 치환율 변화에 따른 고성능 콘크리트의 특성분석

To analyze possibility for high performance concrete that massively displaces blast furnace slag, this study analyzed the characteristics of concrete by blast furnace slag displacement rate changes, and the results are summarized as follows. Firstly, as for fresh concrete characteristics, flow tended to increase and air amount decreased with increase in blast furnace slag displacement rate, and settling time was shown delayed. As for hardened concrete characteristics, in conditions where blast furnace slag displacement rate increased up to 50%, the compressive strength decreased below OPC at early age, however at age 28 days, its level was no less than that of OPC, and as for temperature rise by simple insulation, it decreased as displacement rate increased at early stage of hydration, but in the latter stage, hydration progress slowed down and hydration heat increased.

본 연구에서는 고로슬래그 미분말을 다량 치환하는 고성능 콘크리트의 가능성을 분석하기 위해, 고로슬래그 미분말의 치환율 변화에 따른 콘크리트의 특성을 분석하였는데, 그 결과를 요약하면 다음과 같다. 먼저, 굳지않은 콘크리트의 특성으로 유동성은 고로슬래그 미분말의 치환율이 증가함에 따라 증가하는 경향을 나타내었고, 공기량은 감소하는 경향을 나타내었으며, 응결시간은 지연되는 것으로 나타났다. 경화콘크리트의 특성으로 고로슬래그 미분말의 치환율이 50%까지 증가하는 조건에서의 압축강도는 초기재령에서 OPC보다 저하 하였지만 재령 28일에서는 OPC와 동등이상의 수준을 나타내었으며, 간이 단열에 의한 온도 상승량은 수화 초기에 치환율이 증가 할수록 감소였으나 후반부에서는 수화가 서서히 진행되어 수화열이 증가하는 것으로 나타났다.