An Effect on Early Temperature of Placing Concrete Affecting Compressive Strength of Concrete

콘크리트 타설 초기온도가 압축강도에 미치는 영향

The strength of concrete is developed by cement hydration reaction influenced by the circumferential temperatures. In this study, therefore, the experiments are conducted and evaluated about the characteristics as changes of early concrete placing temperature and curing temperature to understand the effects of the temperature which influences concrete properties. The results of the experiments changing the early concrete placing temperature in 5$^{\circ}C$ and 10$^{\circ}C$ are followed. In case of conducting standard concrete curing, early compressive strength development rate of the concrete which had low placing temperature was low, but it was shown that early compressive strength development rate was not affected by low placing temperature in age 28 days of concrete. In case of conducting outdoor curing in winter, early compressive strength development rate of the concrete which had high placing temperature was high in all test specimens. As a results, early compressive strength development of concrete was influenced by temperature of early concrete, but after aging 28 days of concrete, it was influenced by curing temperature rather than temperature of early concrete.

콘크리트의 압축강도는 시멘트 수화반응에 의하여 발현되는 것으로, 이러한 수화반응은 온도에 민감한 영향을 받게 된다. 이에 본 연구에서는 온도에 의한 콘크리트의 영향을 확인하고자 콘크리트의 타설 초기온도 변화 및 양생 조건의 변화에 따른 특성을 실험적으로 평가하였다. 콘크리트의 타설 초기온도를 5$^{\circ}C$, 20$^{\circ}C$로 변화시켜 실험한 결과, 표준양생을 실시한 경우 타설 온도가 낮은 배합에서 재령 3일 이전까지 강도가 낮았으나, 재령 7일 이후에서는 강도가 높아지는 현상이 확인 되었다. 그러나 재령 28일에서는 두 배합의 압축강도 차가 미미하여 온도에 따른 영향이 크지 않은 것으로 확인 되었다. 기건양생을 실시한 경우는 모든 시험체에서 타설 초기온도가 높은 배합이 높은 강도를 나타내었다. 이러한 콘크리트의 타설 초기온도에 따른 압축강도 특성은 SEM관찰 결과 미세구조의 수화양상을 통하여 그 특성을 확인할 수 있었다.