Study on the Water Penetration in Mortar by Water Pressure

수압에 따른 모르타르내 수분침투에 관한 연구

Concrete is a type of porous materials and is physically and chemically damaged due to exposure to various environments from the placing to the service life. These reactions affect the corrosionof steel bars applied in concrete and that decreases the durability life and strength of such steel bars. Thus, it is very important to insert rust inhibitors into steel bars in the case of a deterioration element that exceeds the critical amount of corrosion in the location of steel bars. However, it is very difficult to guarantee corrosion resistance at the location of steel bars using conventional technology that applies corrosion inhibitors only on the surface of concrete. This study attempts to develop a method that penetrates corrosion inhibitors up to the location of steel bars and investigate the penetration depth of corrosion inhibitors by verifying moisture migration in concrete under an applied pressure.

콘크리트는 다공성 재료로써 타설 직후부터 사용년한 동한 각종 환경에 노출되어 물리적 혹은 화학적인 영향을 받게 된다. 특히, 외부에 존재하는 황산염, 염화물 이온, 이산화탄소 등과 같은 유해성분들은 장기간에 걸쳐 용액 혹은 기체 상태로 콘크리트 내부로 침투되어 콘크리트 구성물들과 물리적 혹은 화학적 상호작용을 일으켜 콘크리트내에 매설된 철근의 부식을 야기 시켜 콘크리트의 내구년한과 내력을 감소시키게 된다. 따라서 철근위치까지 유해한 열화인자가 임계부식량을 초과하는 경우 방청성분을 철근위치까지 확실하게 침투시키는 것이 매우 중요하나, 현재와 같이 콘크리트 표면에 방청제를 도포하여 침투 시키는 기술개발만으로는 철근위치에서의 방청성 확보가 곤란한 실정이다. 본 연구진은 철근위치까지 방청제를 침투시키기 위한 연구개발을 추진하고 있으며, 이를 공학적으로 규명하기 위하여 압력 하에서 콘크리트내로의 수분이동과 같이 방청제에 따른 방청제 침투깊이를 명확히 규명할 필요가 있다. 이를 규명하기 위하여 모르타르를 사용하여 수압에 따른 침투깊이 및 침투량을 측정하여 침투량과 침투 깊이와의 관계 및 가압 시간에 따른 침투 깊이와 침투량을 실험을 통하여 측정하여 침투계수 및 확산계수를 산정하고 가압시간과 수압에 따른 모르타르내에 침투깊이를 예측하였다.