Hydration Heat Properties of High Flowing Self-Compacting Concrete with Normal Strength

보통강도 고유동 자기충전 콘크리트의 수화발열 특성

This research carries out experiments for hydration exothermic rate and adiabatic temperature rise of concrete to examine the characteristics of the hydration heat of high flowing self-compacting concrete with a normal strength. As a result of the hydration exothermic rate experiment, the high flowing self-compacting concrete that used Lime stone powder and fly ash as polymers shows that its hydration heat amount reduces due to the reduction of unit cement. The result measured the adiabatic temperature rise of concrete presents that high flowing self-compacting concrete having lots of binder contents has a good performance in temperature reduction due to the effect of polymer and that triple adding high flowing self-compacting concrete has a similar temperature rise speed with conventional concrete. As a result of the research, high flowing self-compacting concrete shows a better temperature reduction performance for the binder content per unit than conventional concrete. In addition, it is judged that triple adding high flowing self-compacting concrete with a specified concrete strength 30 MPa is more beneficial in temperature reduction and early hydration heat than double adding high flowing self-compacting concrete.

본 연구에서는 보통강도 고유동 자기충전 콘크리트의 수화발열 특성을 알아보기 위하여 미소수화열 시험 및 간이 단열에 의한 콘크리트 온도 상승량 실험을 실시하였다. 미소수화열 시험을 실시한 결과 석회석미분말 및 플라이애시를 혼화재로 사용한 고유동 자기충전 콘크리트는 단위시멘트량 감소로 수화발열량이 감소하였다. 간이 단열에 의한 콘크리트 온도 상승량을 측정한 결과 분체량이 많은 고유동 자기충전 콘크리트가 혼화재의 영향으로 온도저감 성능이 우수 하며, 3성분계 고유동 자기충전 콘크리트의 경우 일반콘크리트와 유사한 온도상승속도를 나타내었다. 이러한 결과 고유동 자기충전 콘크리트가 일반콘크리트보다 상대적으로 높은 단위 분체량에 대한 온도저감 성능이 우수 하며, 설계기준강도 30MPa의 3성분계가 2성분계 고유동 자기충전 콘크리트보다 온도저감 및 초기 수화발현에 유리할 것으로 판단된다.