초록
$TiO_2-V_2O_5$ sol was fabricated using sol-gel method and $TiO_2-V_2O_5$ thin films were fabricated using dip-coating method. $V_2O_5$ sol was added 0.01mo1e, 0.03mo1e, 0.05mo1e into $TiO_2$ sol. Viscosity of sol increased fast from about 1,000 minutes and sol began gelation from about 10,000 minutes. As a results of crystalline properties, $V_2O_5$ peaks were not found despite of $V_2O_5$ addition. Endothermic reaction occurred due to evaporation of solvent and dissociation of OH at $80^{\circ}C$. Exothermic reaction occurred due to combustion and oxidation of solvent at $230^{\circ}C$, occurred to combustion and oxidation of alkyl group at $350^{\circ}C$. Thickness of thin films increased $0.1{\sim}0.25{\mu}m$ every a dipping.