Preparation and Characterization of Sol-Gel Derived High-k $SrTa_2O_6$ Thin Films

$SrTa_2O_6$(STA) thin films were fabricated by sol-gel method. The films annealed below $700^{\circ}C$, showed amorphous phase and crystallization phase was observed after annealing over $800^{\circ}C$. From high frequency capacitance-voltage measurements, 24nm thick STA thin film annealed at $900^{\circ}C$, has an EOT of 5.7nm and a dielectric constant of 16. Leakage current characteristics were improved by the insertion of chemical oxide between STA and Si. Leakage current densities are around $3.5{\times}10^{-7}A/cm^2$ at 5V for the structure inserted chemical oxide but $1.4{\times}10^{-6}A/cm^2$ at 5V without chemical oxide.