Growth and characterites for CdSe single crystal grown by using sublimation method

승화법에 의한 CdSe 성장과 특성

CdSe single crystal was grown by sublimation method in the two-step vertical electric furnace. This CdSe single crustal had hexagonal structure whose lattice constants of $a_0$ and $c_0$ were measured $4.299\;{\AA}$ and $7.009\;{\AA}$ by extrapolation method, respectively. CdSe single crystal was n-type semiconductor values were measured from Hall data by Van der Pauw method in the room temperature. Mobility tends to increase in proportion to $T^{3/2}$ from 33K to 130K due to impurity scattering. but mobility tends to decrease in proprtion to $T^{-3/2}$ from 130K to 293K due to lattice scattering. CdSe thin film was made by electron beam evaporation technique had also hexagonal structure. The grain size of this thin film was grown to $1{\mu}m$ as a result of annealing in the vapor of Ar or Cd. Annealde CdSe thin film was n-type semiconductor whose carrier density had about $7{\times}10^{12}cm^{-3}$ and its mobility had about $1.6{\times}10^3cm^2/V$ sec at room temperature.