A Study on Mechanical Properties of Wood-Polymer Composites due to Environmental Characteristic

목재 고분자 복합재료의 환경 특성에 따른 기계적 물성연구

Polypropylene as a matrix has been used for wood polymer composites(WPC). In preparing WPC, the coupling agent, Polypropylene grafted Maleic Anhydride(PP-G-MA) was used in order to obtain a good interfacial bonding force between matrix and fillers and dispersion of wood powders. In this study, the effects of wood powder contents and water absorption on the mechanical properties were experimentally investigated. The tensile strength and flexural strength of composites reached its peak value when the wood powder content was around 60 wt%. However, the peak value of the impact was observed about 30 wt% of wood powder content. The tensile strength and flexural strength increase with increasing the wood power contents. But the impact strength decrease with increasing the wood powder contents. The slight change was observed with the water absorption in the WPC. The optimal condition of the compositions such as Anti-oxidant and UV stabilizers for the outdoor application was suggested in this research.