Structural and Magnetic Properties of $FePt-B_x\;at.\%$ (X=5, 10, 15, 25 and 33) thin Film by Post-Annealing

Multi-layer film of $MgO/(FePt-B)_{50nm}/ MgO$ was deposited on Si(100) substrates by RF magnetron sputtering. The boron chips were uniformly placed oil tile FePt target. The boron content of thin film was found to be about 5, 10, 15, 25 and $33 at\%$ by using a CAMECA SX-51 wavelength dispersive spectroscopy (WDX). It is observed that X-ray diffraction patterns of FePt-B film by post-annealing exhibited a transformation from disordered fcc structure to ordered $Ll_0$ phase with fct structure from around $400^{\circ}C$. By adding B, annealing temperature for ordering is about $200^{\circ}C$ lower than that of pure FePt. This remarkable decrease of the annealing temperature is closely related to the high diffusivities of Fe and Pt associated with the defects caused by movements of B atoms. The maximum coercivity(Hc) for FePt films was found to be ${\~}$13 kOe after annealing at $600^{\circ}C$ for 1hr.