Abstract
Dry sliding wear behavior of electro-pressure sintered Co, $Co-20\;wt.\%$ CuSn and $Co-20\;wt.\%$ WC composites were investigated. Wear tests of the materials were carried out using a pin-on-disk wear tester at various loads of 10N-100N under a constant sliding speed condition of 0.38m/s against glass ($83\%\;SiO_2$) beads. Sliding distances were varied with a range of $100m{\sim}600m$. A scanning electron microscopy was used to examine morphologies of worn surfaces, cross-sections, and wear debris. The $Co-20\;wt.\%$ WC composite had the highest and the $Co-20\;wt.\%$ CuSn composite showed the lowest wear resistance among the tested materials. All specimens exhibited low friction coefficients ranging from 0.12 to 0.4 at the applied load of 100N.