Annealing Temperature Properties of SBT Thin Film for Semiconductor Device

반도체 소자용 SBT 박막의 후속 열처리 특성

The SBT$(Sr_{0.8}Bi_{2.4}Ta_2O_9)$ thin films for semiconductor device were deposited on Pt-coated $Pt/TiO_2/SiO_2Si$ wafer by RF magnetron sputtering method at $400[^{\circ}C]$ and annealed at the temperature range from $600[^{\circ}C]$ to $850[^{\circ}C]$. The top electrodes(Pt) were deposited on SBT thin film by DC sputtering method. The crystallinity of SBT thin films were increased with increase of annealing temperature in the temperature range of $600[{\circ}C]\sim850[^{\circ}C]$. The annealing temperature properties were to be most excellent in the case of annealed SBT thin film at $750^{\circ}C]$. And, the maximum remanent polarization$(2P_r)$ and the coercive electric field$(E_c)$ at annealing temperature of $750[^{\circ}C]$ obtained about $11.60[{\mu}C/cm^2]$ and 48[kV/cm], respectively. Specially, it was seen that fatigue properties does not change in $10^{10}$ switching cycle.