초록
The melting temperature and critical temperature (Tc) of YBa$_2$Cu$_3$Ox with deferent content impurities of PbO and BaPbO$_3$ were studied. When the PbO was used as addition in YBa$_2$Cu$_3$Ox, although the melting point could be reduced, the superconductivity (the transition wide, ΔTc) became poor. From the XRD pattern of the sintered mixture of YBa$_2$Cu$_3$Ox and PbO it was known that there is a reaction between YBa$_2$Cu$_3$Ox and PbO, and the product is BaPbO$_3$. In the process of the reaction the superconducting phase of YBa$_2$Cu$_3$Ox was decreased and in the sample BaPbO$_3$became the main phase. Therefore the superconductivity was reduced. BaPbO$_3$was chosen as the impurity for the comparative study. The single phase BaPbO$_3$was synthesized by the simple way from both mixtures of BaPbO$_3$and PbO, BaPbO$_3$and PbO$_2$. Deferent contents of BaPbO$_3$(10%, 20%, 30%) were added in the YBa$_2$Cu$_3$Ox. By the phase analysis in the XRD patterns it was proved that there were not reactions between YBa$_2$Cu$_3$Ox and BaPbO$_3$. When BaPbO$_3$was used as impurity in YBa$_2$Cu$_3$Ox the superconductivity was much better than PbO as impurity in YBa$_2$Cu$_3$Ox But the melting point of YBa$_2$Cu$_3$Ox with BaPbO$_3$could not be found when the temperature was lower than 1000 $^{\circ}C$ in the DTA measurement.