The effect of electrical properties by gas ratio on $Bi_{3.25}La_{0.75}Ti_3O_{12}$ thin films deposited by RF magnetron sputtering during being annealed

RF magnetron sputtering으로 제작한 BLT 박막의 후열처리 시 가스비 변화에 따른 전기적 특성에 관한 연구

The role of gas ratio with the crystallization behavior and electrical properties in $Bi_{3.25}La_{0.75}Ti_3O_{12}$(BLT) thin films by rf magnetron sputtering method has not been precisely defined. In this work, the ferroelectric properties of these films with gas variation was investigated. BLT thin films were deposited on the Pt/Ti bottom electrode by rf magnetron sputtering method and then they were crystallized by rapid thermal annealing (RTA). The experiment showed that all BLT films indicated perovskite polycrystalline structure with preferred orientation (020) and (0012). And no pyrochlore phase was observed. The fabricated film annealed with $O_2$ of 15 sccm showed that value of leakage current was $9.67{\times}10^{-7}A/cm^2$ at 50kV /em, and the value of remanent polarization (2Pr=Pr+-Pr-) was $11.8{\mu}C/cm^2$. Therefore we induce access to memory device application by rf-magnetron sputtering method in this report.