초록
$Sr_xBa_{1-x}Nb_2O_6$(SBN, $025{\leq}x{\leq}0.75$) ceramic is a ferroelectric material with tetragonal tungsten bronze (TTB) type structure, which has a high pyroelectric coefficient and a nonlinear electro-optic coefficient value. In spite of its advantages, SBN has not been investigated well compared to other ferroelectric materials with perovskite structure. In this study, SBN thin film was manufactured by ion beam sputtering technique using the prepared SBN target in Ar/$O_2$ atmosphere. SBN30 thin film of 500 ${\AA}$ was pre-deposited as a seed layer on Pt(l00)/$TiO_2$/$SiO_2$/Si substrate followed by SBN60 deposition up to 4500 ${\AA}$ in thickness. SBN60/SBN30 layer was deposited at different Oxygen amount of 0, 8.1, 17, and 31.8 sccm, respectively. The crystallinity and orientation behavior as well as electric properties of SBN60/SBN30 multi-layer were examined. The deposited layer was uniform and the orientation was shown primarily along (001) plane from XRD pattern. The crystal structure and the electric properties depended on the Oxygen amount, heating temperature and was the best at O2 = 8.1 seem, $750^{\circ}C$. In electric properties of Pt/SBN60/SBN30/Pt thin film capacitor prepared, the remnant polarization (2Pr) value was 13 ${\mu}C/cm^2$, the coercive field (Ec) 75 kV/cm, and the dielectric constant 1492, respectively.