Analysis of wear properties in Zr alloys with variation of Nb and Sn content

Zr 합금에서 Nb과 Sn의 함량에 따른 마멸특성분석

In order to evaluate the effect of alloying elements (Nb and Sn) on the wear resistance of advanced Zr fuel claddings, sliding wear tests have been performed in room temperature air and water and these results were compared with those of commercial alloys such as Zircaloy-4, A and B alloys. As a result, the advanced Zr fuel claddings have a similar wear resistance compared with the commercial alloys. The wear resistance of the advanced Zr fuel claddings is closely releted to the content of Nb and Sn even though the effects of transition elements are involved in deforming wear properties. In the tested specimens with similar Sn content, wear volume became down to a minimum at $0.4\;wt\;\%$ Nb, then rapidly increased at 1.0 wt Nb. This behavior results in the variation of grain size with alloying contents. But Sn did not have a significant effect on the wear volume of advanced Zr fuel claddings below $1.1\;wt\%$. The relationship between alloying elements and wear behaviour was evaluated and discussed using material compatibility factor.