The characteristics of AlN buffered GaN on ion beam modified Si(111) substrates

Si(111) 위에 Ion beam 처리 후 AlN layer를 완충층으로 이용하여 성장시킨 GaN의 특성

The growth of GaN on Si is of great interest due to the several advantages : low cost, large size and high-quality wafer availability as well as its matured technology. The crystal quality of GaN is known to be much influenced by the surface pretreatment of Si substrate[1]. In this work, the properties of GaN overlayer grown on ion beam modified Si(111) have been investigated. Si(111) surface was treated RIB with 1KeV-N$_2$$\^$+/(at 1.9 ${\times}$ 10$\^$-5/) to dose ranging from 5${\times}$10$\^$15/ to 1${\times}$10$\^$17/ prior to film growth. GaN epilayers were grown at 1100$^{\circ}C$ for 1 hour after growing AlN buffer layers for 5∼30 minutes at 1100$^{\circ}C$ in Metal Organic Chemical Vapor Deposition (MOCVD). The properties of GaN epilayers were evaluated by X-Ray Diffraction(XRD), Raman spectroscopy, Photoluminescence(PL) and Hall measurement. The results showed that the ion modified treatment markedly affected to the structural, optical and electrical characteristic of GaN layers.